High Aluminate Cement

Categories Refractories
Payment Terms: L/C, T/T, D/P, Paypal, Western Union
Trade Terms: CIF
Material: Aluminium Silicate
Main Markets: Global
Type: High-temperature Adhesives
Place of Origin: china
Category: Ceramic Fiber Paper
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    High Aluminate Cement

    The aluminate cement can resist a high temperature at which a relative high stength still remains its refractoriness increases with the content of CaO, therefore it is suitable for making refractoryconcerte as a bonder, Depending on the refractory aggregates(fireclay, high alumina) used, the refractory concerte made of the cement can be used below 1800 degree.
    1. Type: CA50-G7
    (1) Chemical Analysis
    Al2O3: 51% min. SiO2: 8.0% Max. Fe2O3: 2.5% Max. CaO: 33.0-35.0%
    (2) Physical Properties
    Initial set time: 0: 30mins min.
    Final set time: 6h: 00 max
    Specific surface area: 300m2/kg min.
    Flexural strength
    1 day 6.5Mpa min.
    3 days 7.5Mpa min.
    Compressive strength
    1 day 50Mpa min.
    3 day 60Mpa min
    2. TYPE: CA50-G9
    (1)Chemical Analysis
    Al2O3: 52.0-55.5% SiO2: 6.5% Max. Fe2O3: 2.0% Max. CaO: 33.5-35.5%
    (2) Physical Properties
    Initial set time: 1h: 30mins min.
    Final set time: 6h: 00 max
    Specific surface area: 400m2/kg min.
    Flexural strength
    1 day 8.0Mpa min.
    3 days 10.0Mpa min.
    Compressive strength
    1 day 70.0Mpa min.
    3 day 80.0Mpa min
    3. TYPE: CA50-Fused
    (1) Chemical Analysis
    Al2O3: 50% min. SiO2: 5.5% max. Fe2O3: 2.5% max. CaO: 38.0% max
    MGO: 1.0% max. TiO2: 4.0% max. Na2O+K2O 0.5% max
    (2) Physical Properties
    Initial set time: 2h min.
    Final set time: 8h: 00 max
    Specific surface area: 400m2/kg min.
    Flexural strength
    1 day 10.0Mpa min.
    3 days 11.0Mpa min.
    Compressive strength
    1 day 75Mpa min.
    3 day 80Mpa min
    4. TYPE: CA70 (Sintered)
    (1) Chemical analysis
    Al2O3: 68.0%-70.0% SiO2: 0.3-0.8% Fe2O3: 0.2-0.5% max.
    CaO: 28.5-30.5% max
    (2) Physical Properties
    Initial set time: 2hrs min.
    Final set time: 6h: 00 max
    Specific surface area: 370-550m2/kg min.
    Flexural strength
    6 hours 3.0% min.
    1 day 7.0Mpa min.
    3 days 8.0Mpa min.
    Compressive strength
    6hours 15-30Mpa
    1 day 40-45Mpa
    3 day 55-70Mpa
    5. TYPE: CA80 (Sintered)
    (1) Chemical Analysis
    Al2O3: 78% min. SiO2: 0.5% max. Fe2O3: 0.5% max. CaO: 19 % max
    MGO: 0.5% max. TiO2: 0.3% max. Na2O+K2O: 0.7% max.
    (2) Physical Properties
    Initial set time: 30mins min.
    Final set time: 6h: 00 max
    Specific surface area: 650m2/kg min.
    Flexural strength
    1 day 4.0Mpa min. 3 days 5.0Mpa min.
    Compressive strength
    1 day 30Mpa min. 3 day 35Mpa min&
    Quality High Aluminate Cement for sale
    Send your message to this supplier
     
    From:
    To: Taixing Well Import and Export Trade Co. Ltd.
    Subject:
    Message:
    Characters Remaining: (0/3000)
     
    Find Similar Products By Category:
    Inquiry Cart 0

    Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

    Copyright © 2009 - 2019 hfcletter.com. All rights reserved.